M3D SCARA

 
 

The M3D Scara

The largest of our models and by far the most capable. Equipped with a full 360 degree range of motion and an advanced robotic arm it builds upon the feature set of every model before it. This printer is able to create prints of very large size with amazing accuracy and combined with our proprietary printing technology (BMPD) which expands the usable build media and increase’s the speed of the entire process start to finish, the printer allows for virtually limitless options for your designs and prints.

M3D SCARA SPECS:

  • Dimensional accuracy: ± 0.5 mm

  • Maximum build size: X/Y- 58" Diameter Circle (1473mm)
    Z- 23” (584mm)

  • Common layer thickness: 4mm down to 0.2 mm

  • Max build rate: 1,000 ml per hr.

  • Max build weight: 8 kilos per hr.

  • Feedstock Extruder Assembly: 1 to 5 Liters container

  • Regular environment temp.: 210C at 40% humidity

  • Nozzle diameter: 0.4mm up to 5.0mm

  • Nozzle material: Stainless steel, Nickle Coated Steel or plastic

  • Printing table: Acrylic (Adhesion sheets recommended, i.e. ABS)

  • Software : Metallic 3D Fabricate GUI

  • File types: STL and OBJ

  • Browser requirements: Accessible via any web browser

  • Network connectivity: wireless on any device

  • Power requirements: 110-220V, 50-60 Hertz, 24V ~10 amps, ~240 Watt

  • External dimensions (WxLxH): W-30” L-12” H-44”

  • Weight: 23 kg (50 LBS)

3D Printer Set consists of:

  • 1x "METALLIC 3D" BMPD 3D printer (Made in USA)

  • 1x Feedstock Container 950 ml net for Extruder Assembly 10x steel Nozzles 0.4mm

  • 1x Printing table Acrylic

  • 10x Adhesion sheets ABS

  • 20 kg Binder

  • Documentation

BUILD MEDIA:

METALS:

  • STAINLESS STEEL

  • TUNGSTEN STEEL

  • TOOL STEEL

  • COPPER

  • NICKEL

  • INCONEL

  • COBALT CHROMIUM MOLYBDENUM

  • TITANIUM

  • ALUMINUM

  • PRECIOUS METALS (Gold, Platinum, Palladium, Sterling Silver)

CERAMICS:

  • ALUMINA

  • ZIRCONIA

  • SILICON NITRIDE

  • GLASS

CERMETS:

  • TUNGSTEN CARBIDE/COBOLT (WC-Co)

  • METAL-BONDED DIAMOND COMPOSITES